RTP 100.5
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tgbsWL_RTP-100-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18mm, injection molding | 1.0 | % | ASTM D955 |
| 6.35mm, injection molding | 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 2760 | MPa | ASTM D638 |
| Tensile Strength | 38.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 10 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 2070 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 52.0 | MPa | ASTM D790 |
| Compressive Strength | 48.0 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, injection molded | 127 | °C | ASTM D648 |
| 1.8 MPa, unannealed, injection molded | 121 | °C | ASTM D648 |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.16 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammibility, UL 94, was tested in accordance with RTP Company methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 193 - 227 | °C | |
| Middle Temperature | 193 - 227 | °C | |
| Front Temperature | 193 - 227 | °C | |
| Mold Temperature | 32.0 - 66.0 | °C | |
| Injection Pressure | 69.0 - 103 | MPa |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 2505 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Solanyl® BP blend 40R | Rodenburg Biopolymers B.V. | Biodeg Polymers | Solanyl® BP blend |
| NORDEL™ IP 4725P | The Dow Chemical Company | EPDM | NORDEL™ |
| Bergamid™ B70 G33 U OR262 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Sylvin 4200-88UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |