Amilan® CM1017XL3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tgOWUv_Amilan-CM1017XL3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amilan® CM1017XL3 is a Polyamide 6 (Nylon 6) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | Internal Method | |||
| 1.00 mm 1 | 0.70 to 1.1 | -- | % | |
| 3.00 mm 2 | 1.2 to 1.8 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.8 | -- | % | |
| Saturation, 23°C | 11 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| R-Scale, 80°C | 80 | -- | ||
| R-Scale, 23°C | 119 | 90 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 110 | 100 | MPa | |
| 23°C | 80.0 | 35.0 | MPa | |
| 80°C | 25.0 | 20.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Yield, 23°C | 1.5 | -- | % | |
| Break, 23°C | 38 | 50 | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 3800 | 3600 | MPa | |
| 23°C | 2800 | 800 | MPa | |
| 80°C | 700 | 300 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 135 | 125 | MPa | |
| 23°C | 110 | 40.0 | MPa | |
| 80°C | 40.0 | 25.0 | MPa | |
| Compressive Stress (23°C) | 80.0 | -- | MPa | ISO 604 |
| Shear Strength (23°C) | 70.0 | 65.0 | MPa | ASTM D732 |
| Taber Abrasion Resistance (1000 Cycles) | 3.00 to 4.00 | -- | mg | ISO 9352 |
| Coefficient of Friction - vs. Metal 3 | 0.150 to 0.200 | -- | Suzuki Method |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 3.5 | -- | kJ/m² | |
| 23°C | 5.0 | 31 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | No Break | -- | ||
| 23°C | No Break | -- |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 182 | -- | °C | ISO 75-2/B |
| Melting Temperature | 225 | -- | °C | DSC |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1900 | -- | J/kg/°C | |
| Thermal Conductivity | 0.25 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 to 1.0E+15 | 1.0E+11 to 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant 4 | IEC 60250 | |||
| 23°C, 50 Hz | 4.10 | 9.00 | ||
| 23°C, 1 kHz | 3.90 | 8.00 | ||
| 23°C, 1 MHz | 3.40 | 4.50 | ||
| Dissipation Factor 5 | IEC 60250 | |||
| 23°C, 50 Hz | 0.070 | 0.10 | ||
| 23°C, 1 kHz | 0.060 | 0.11 | ||
| 23°C, 1 MHz | 0.030 | 0.13 | ||
| Arc Resistance 6 | 120 | -- | sec | UL 746 |
| Comparative Tracking Index (CTI) | 600 | -- | V | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.794 mm) | V-2 | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x1mm |
| 2 . | 80x80x3mm |
| 3 . | Without Lubrication |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene HFR8284 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| TRANSMARE® 19HT20-0.002 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| TRIBOCOMP® POM TS14 | EPIC Polymers | Acetal (POM) Copolymer | TRIBOCOMP® |
| Chemlon® JW21 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Pacrel® 6375N | Nanjing Jinling OPTA Polymer Co., Ltd. | TPV | Pacrel® |