Pro-fax 8623
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | teD4wl_Pro-fax-8623.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax 8623 very high impact polypropylene copolymer is available in pellet form. This resin is typically used in extrusion and injection molding applications and offers excellent cold temperature impact resistance. An ASTM and ISO-based versions of the technical datasheet are available for Pro-fax 8623 For regulatory compliance information see Pro-fax 8623 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.898 | g/cm³ | ASTM D792B |
| -- | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 23.0 | MPa | ASTM D638 |
| Yield, 23°C | 22.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.0 | % | ASTM D638 |
| Yield, 23°C | 10 | % | ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant 2 | 1040 | MPa | ASTM D790A |
| 23°C | 1020 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 3.3 | kJ/m² | |
| 23°C | 82 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | No Break | ASTM D256A | |
| 23°C | 65 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 77.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 68.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 46.0 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202 A | RTP Company | Nylon 6 | RTP |
| TAISOX 9001 | Formosa Plastics Corporation | HDPE | TAISOX |
| Fainplast PVC PK 55/KN | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| KetaSpire® KT-810 | Solvay Specialty Polymers | PEEK | KetaSpire® |
| Hostacom PPR 1042 101070 | LyondellBasell Industries | PP Copolymer | Hostacom |