Wellamid® 22LH-WBK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tdiQHd_Wellamid-22LH-WBK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Wellamid® 22LH-WBK is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.8 to 2.2 | % | |
| Flow : 23°C | 1.6 to 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 25 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 277 to 293 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 266 to 282 | °C | |
| Nozzle Temperature | 266 to 293 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K1011 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| NEFTEKHIM PP 1500J (T30G) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 2033Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| Nypol® PA A3 G15 P7 M1 S1 NTLA014 NR335 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Axpoly® r-PP52 1000 | Axion Polymers | PP Copolymer | Axpoly® |