Celstran® PEHD-GF60-01
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | td5ebS_Celstran-PEHD-GF60-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 58% long strand glass fiber reinforced high density polyethylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.51 | g/cm³ | ASTM D792 |
| -- | 1.50 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 15200 | MPa | ASTM D638 |
| 23°C | 13600 | MPa | ASTM D638 |
| 93°C | 7170 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 161 | MPa | ASTM D638 |
| Fracture, 23°C | 113 | MPa | ASTM D638 |
| Fracture, 93°C | 49.0 | MPa | ASTM D638 |
| Fracture | 91.0 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.5 | % | ASTM D638 |
| Fracture | 1.4 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 11700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 121 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 200 - 210 | °C | |
| Middle Temperature | 210 - 220 | °C | |
| Front Temperature | 220 - 230 | °C | |
| Nozzle Temperature | 230 - 240 | °C | |
| Processing (Melt) Temp | 230 - 240 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 230 to 240°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Acetate 105E1R26029 Clear, Trsp | Eastman Chemical Company | CA | Tenite™ Acetate |
| TOTAL Polystyrene Crystal 525B | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Delta ABR-1G30/1 | Delta Polymers | ABS | Delta |
| European Santicizer® 160 | Ferro Corporation | Plasticizer | European |
| Karina IVORY PVC COMPOUND -E 907-35/ 1-AY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |