Durethan® AKV 50 000000
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tbwuYT_DurethanAKV50000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 50% glass fibers, injection molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.57 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 300°C, 3.00mm 1 | 1.3 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 3.00mm 2 | 0.030 | -- | % | ISO 2577 |
| Flow direction : 300°C, 3.00mm 3 | 0.23 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 3.00mm 4 | 0.020 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.4 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 290 | 160 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 15700 | 10700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 220 | 170 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 14000 | 10300 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | -- | 235 | MPa | ISO 178/A |
| 23°C 6 | 370 | 250 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.0 | 5.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GR, 14-160, GF50 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 15 | kJ/m² | ISO 179/1eA |
| 23°C | 19 | 23 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 100 | 100 | kJ/m² | ISO 179/1eU |
| 23°C | 95 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 11 | 11 | kJ/m² | ISO 180/1A |
| 23°C | 14 | 18 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 230 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 263 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (3.20 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 400 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 400 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 30H1 V25 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Wellamid® NY1875-BK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Ducaseal Dynamic | Dugdale Plc | PVC, Flexible | Ducaseal |
| Ecomass® 1080CO94 | Ecomass Technologies | Nylon, Unspecified | Ecomass® |
| Honeywell PCTFE P7500HS | Honeywell | PCTFE | Honeywell PCTFE |