TECHNYL® A 218HP V35 BLACK 21N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tb3GSE_TECHNYL-A-218HP-V35-BLACK-21N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218HP V35 Black 21N is a polyamide 6.6, reinforced with 35% of glass fiber, heat stabilized, for injection moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.39 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.46 | -- | % | |
| Molding Shrinkage Isotropy | 0.770 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10700 | 7000 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 170 | 107 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.8 | 5.6 | % | ISO 527-2/1A |
| Flexural Modulus | 8700 | -- | MPa | ISO 178 |
| Flexural Stress | 250 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 75 | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 247 | -- | °C | ISO 75-2/Af |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE 5502 (US) | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| XANTAR® F 23 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| AXELERON™ GP 6314 BK CPD | The Dow Chemical Company | LLDPE | AXELERON™ |
| Lucofin® 7410 HFFR | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| LNP™ LUBRICOMP™ LX91475 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |