TUFNYL® RGF 33 HR NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SRF Ltd. |
| Trademark: | TUFNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | taN4po_TUFNYL-RGF-33-HR-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, 33% Glass fiber reinforced with enhanced hydrolytic resistance material for injection molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 to 0.30 | % | Internal Method |
| Water Absorption (Equilibrium) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 95 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 175 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 255 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 93.2 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LTR662 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Spartech Polycom PP7230U | Spartech Polycom | PP Copolymer | Spartech |
| Grupo IDESA HIPS HI-700-S-01 | Grupo IDESA, S.A. de C.V. | SBC | Grupo IDESA HIPS |
| KOPA® KN153HB40BL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Lucet® N145-LD | LG Chem Ltd. | Acetal (POM) Copolymer | Lucet® |