LNP™ STAT-KON™ PFD06 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | taGhEU_LNP-STAT-KON-PFD06-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON PFD06 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PF-30 Product reorder name: PFD06 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 1.2 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.38 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.50 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.91 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11700 | MPa | ASTM D638 |
| Tensile Strength (Break) | 159 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 241 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 910 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 206 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 to 6.0 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6914 NA023 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Pyramid™ PEI II2250 | Polymics, Ltd. | PEI | Pyramid™ PEI |
| ECONAMID® 6ST1 | DOMO Engineering Plastics SPA | Nylon 6 | ECONAMID® |
| LEMALLOY® BX505 | Mitsubishi Engineering-Plastics Corp | PPE+Nylon 6 | LEMALLOY® |
| LNP™ THERMOCOMP™ MFB429 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |