TOTAL Polypropylene PPC 9760
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ta7o8x_TOTAL-Polypropylene-PPC-9760.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPC 9760 is heterophasic copolymer with a Melt Flow Index of 25g/10 min combining good fluidity and mechanical properties. Polypropylene PPC 9760 is characterized by improved stiffness, creep resistance and high impact resistance. Polypropylene PPC 9760 has been developed specifically for the injection moulding of buckets, pails, toys, housewares and garden furniture. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 83 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.5 | % | ISO 527-2 |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 5.5 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 48.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® FF50 | A. Schulman Europe | ABS | RONFALIN® |
| Elastron® G G401.A40.T | Elastron USA, Inc. | SEBS | Elastron® G |
| ESPRENE EPDM 301 | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Luranyl® KR 2402 | ROMIRA GmbH | PPE+PS | Luranyl® |
| LNP™ LUBRICOMP™ EL003 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |