NORYL™ 731 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tZvao8_NORYL731resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PS, HDT 125 |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 11 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.13 | % | ISO 62 |
| 23°C, 24 hr 1 | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2400 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 54.0 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 45.0 | MPa | ASTM D638 |
| Fracture | 40.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 4.0 | % | ASTM D638 |
| Yield | 70 | % | ISO 527-2/50 |
| Fracture 6 | 30 | % | ASTM D638 |
| Fracture | 70 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 2100 | MPa | ASTM D790 |
| -- 8 | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 120 | J/m | ASTM D256 |
| 23°C | 150 | J/m | ASTM D256 |
| -30°C 11 | 11 | kJ/m² | ISO 180/1A |
| 23°C 12 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 800 | J/m | ASTM D4812 |
| -30°C 13 | 55 | kJ/m² | ISO 180/1U |
| 23°C 14 | 60 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 55.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 110 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 15 | 112 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 133 | °C | ASTM D1525, ISO 306/B50 12 16 |
| -- | 135 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 249 - 299 | °C | |
| Middle Temperature | 260 - 304 | °C | |
| Front Temperature | 271 - 310 | °C | |
| Nozzle Temperature | 282 - 310 | °C | |
| Processing (Melt) Temp | 282 - 310 | °C | |
| Mold Temperature | 76.7 - 104 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 mm |
| 16 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT1055-624 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Unichem 4160 | Colorite Polymers | PVC, Unspecified | Unichem |
| HiFill® TPU 85A 0152 S1 | Techmer Engineered Solutions | TPU, Unspecified | HiFill® |
| INEOS HDPE T50-4400-119 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| Iupilon® GPF2040DF | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |