INSPIRE™ 137 (Film Extrusion)
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Braskem Europe GmbH |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tWdHQK_INSPIRE-137-Film-Extrusion-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INSPIRE™ 137 Performance Polymer, is a high melt strength resin which provides bubble stability, low gel content and can be used as blend partner to make more cost effective films on all types of conventional blown film lines. INSPIRE 137 Performance Polymer can be suggested for film and sheet extrusion. INSPIRE 137 Performance Polymer exhibits:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Energy (50 µm) | 4.40 | J | ASTM D5748 |
| Film Puncture Force (50 µm) | 92.0 | N | ASTM D5748 |
| Tensile Modulus | ISO 527-3 | ||
| 2% secant, MD : 50 µm | 624 | MPa | ISO 527-3 |
| 2% secant, TD : 50 µm | 584 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm | 34.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm | 24.0 | MPa | ISO 527-3 |
| MD : Break, 50 µm | 50.0 | MPa | ISO 527-3 |
| TD : Break, 50 µm | 36.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 590 | % | ISO 527-3 |
| TD : Break, 50 µm | 670 | % | ISO 527-3 |
| Dart Drop Impact (50 µm) | 160 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 26 | g | ASTM D1922 |
| TD : 50 µm | 57 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 19 | ASTM D2457 | |
| Haze (50.0 µm) | 36 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 模具间隙：1.0 mm 熔体温度：230°C 放大比：2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8692-66 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ARCEL® ULV (2.00 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| Geon™ Vinyl Flexible C70A0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LNP™ STAT-KON™ WE003ER compound | SABIC Innovative Plastics Europe | PBT | LNP™ STAT-KON™ |
| Pearlthane® 11T92E | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |