ADVANCENE™ EM-5822-AAH
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | ETHYDCO |
| Trademark: | ADVANCENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tU6SoB_ADVANCENEEM5822AAH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADVANCENE™ EM-5822-AAH HDPE Resin is a multipurpose polymer designed tor production of medium to large blow molded containers and parts. Main Characteristics:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 190°C/2.16 kg | 0.17 | g/10 min | ASTM D1238, ISO 1133 |
| 190°C/21.6 kg | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 47.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 27.6 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 14.5 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 9.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 940 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 2% Secant | 924 | MPa | ASTM D790B, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 68.0 | °C | ASTM D648, ISO 75-2/B |
| Brittleness Temperature | < -77.0 | °C | ASTM D746, ISO 974 |
| Vicat Softening Temperature | 131 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 139 | °C | ASTM D3418, ISO 3146 |
| Peak Crystallization Temperature (DSC) | 113 | °C | ASTM D3418, ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® R123 TR25 | Razin™ Engineering Plastics | PP+EPDM | Razalen® |
| Spartech Polycom SCR5-2025 | Spartech Polycom | PP Copolymer | Spartech |
| Vi-Chem PVC VDM87-15E/30E-8814 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Duron PEI 2100 | ProPolymers Inc. | PEI | Duron |
| Paryls® PES F2250 | Youju New Materials Co., Ltd. | PESU | Paryls® |