NYLAFORCE® dynamic A 50
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LEIS Polytechnik - polymere Werkstoffe GmbH |
| Trademark: | NYLAFORCE® dynamic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tT2UmP_NYLAFORCE-dynamic-A-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| produced by feed up-process, polyamide 6.6 + 50% glass fibres, heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.10 to 0.50 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C 2 | -- | 12500 | MPa | |
| 23°C | 18000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| 23°C 3 | -- | 190 | MPa | |
| 23°C | 275 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, 23°C 4 | -- | 4.5 | % | |
| Break, 23°C | 2.9 | -- | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -- | 16 | -- | kJ/m² | |
| 23°C 5 | -- | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -- | No Break | -- | ||
| 23°C 6 | -- | 98 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 7 | 260 | -- | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | 60mm x 60mm x 2mm |
| 2 . | Tested according to ISO 527/ISO 1110 |
| 3 . | Tested according to ISO 527/ISO 1110 |
| 4 . | Tested according to ISO 527/ISO 1110 |
| 5 . | Tested according to ISO 179/ISO 1110 |
| 6 . | Tested according to ISO 179/ISO 1110 |
| 7 . | 10K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 1200H-25 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| DOW™ HDPE LP 8000 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Boda BDF-KR2752 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Hifax CA 1110 G4 LS | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| KOPLA PET KEG1020 | KOPLA Co., Ltd. | PET | KOPLA PET |