Spartech Polycom SC14-2233L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tT0G3y_Spartech-Polycom-SC14-2233L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech SC14-2233L is a medium viscosity nylon 6 resin for injection molding applications that features 33% glass fiber reinforcement. It is heat stabilized and lubricated for good processing characteristics. Nylon 6 resins have good mechanical properties, good toughness at low temperatures, and high thermal stability. They also have excellent chemical resistance and their dielectric properties are very good. A very versatile product for a wide variety of applications, Spartech SC14-2233L is recommended for industrial, transportation, sporting goods and electrical/electronic applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 152 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 7580 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 214 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 222 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 212 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 - 93.3 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 249 - 271 | °C | |
| Middle Temperature | 277 - 288 | °C | |
| Front Temperature | 271 - 288 | °C | |
| Nozzle Temperature | 277 - 288 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 37.8 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 36.0 | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| ACCULOY™ PCA083L | ACLO Compounders Inc. | PC+ABS | ACCULOY™ |
| Badaflex® TPE-S 60A 1000LD | Bada AG | TPE | Badaflex® |
| Cellophane™ XS600 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| ESTOPLAST XU 6100GY02 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |