SPECIALTY PARTIALLY AROMATIC POLYAMIDE BLEND
PARTIALLY AROMATIC PA, 30% CARBON FIBER REINFORCED, 15% PTFE LUBRICATED |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow : 23°C | 0.40 | -- | % | ISO 294-4 |
| Flow : 23°C | 0.15 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.40 | -- | % | ISO 62 |
| Saturated, 23°C | 4.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 22000 | 21000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 230 | 195 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.1 | 2.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 60 | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 9.0 | 10 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 225 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (3.20 mm, Solution A) | 100 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | HB | -- | UL 94 | |
| 0.8 mm | HB | -- | UL 94 | |
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 2000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® STA32 | A. Schulman Europe | ABS | RONFALIN® |
| Celcon® MR270B | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Chemical Resources BPP3500 | Chemical Resources, Inc. | PP Impact Copolymer | Chemical Resources |
| Globalprene® 3741P | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| LNP™ THERMOCOMP™ CF008 compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ THERMOCOMP™ |