Plexiglas® Frosted DR®-66080
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tQZ7Ks_Plexiglas-Frosted-DR--66080.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexiglas® Frosted DR®-66080 is an impact modified thermoplastic acrylic resin formulated for injection molding and extrusion applications. It has a frosted appearance, is heat resistant and provides 10 times the impact resistance of standard acrylics. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 0.80 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 50 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2280 | MPa | ASTM D638 |
| Tensile Strength (Break) | 52.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 38 | % | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 88.9 | °C | |
| 1.8 MPa, Annealed | 79.4 | °C | |
| Vicat Softening Temperature | |||
| -- | 96.1 | °C | ASTM D1525 2 |
| -- | 85.0 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3180 µm) | 84.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0131T1V1 | ASTM D788 |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 176°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BX30WT6617 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Next Nylon 6 Prime Series NST35-01NC | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| ExxonMobil™ LDPE LD 144BR | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Karina WHITE PVC 837-10/ 55-AY-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LubriOne™ GF-1010 40 MS 2 HS Black 37 | PolyOne Corporation | Nylon 6 | LubriOne™ |