Braskem PE ML3602U
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tP7E8T_BraskemPEML3602U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The resin ML3602U is a Linear Low Density Polyethylene indicated for rotational molding. Applications: High mechanical resistance parts large tanks for water Technical, agricultural and automotive parts Water tanks Technical Characteristics: Good surface finishing Excellent processability Standard color for natural parts Excellent balance between stiffness and impact resistance UV and heat stabilization Additives: Weathering resistance UV8 and antioxidants. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.937 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 2.00mm, 10% Igepal, molded, F50 | 22.0 | hr | ASTM D1693 |
| 50°C, 2.00mm, 100% Igepal, molded, F50 | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 13 | % | ASTM D638 |
| Fracture | > 1000 | % | ASTM D638 |
| Flexural Modulus | 740 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | ARM | ||
| -40°C, 3.14mm, rotational molding | 80 | J | ARM |
| -40°C, 6.34mm, rotational molding | 220 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 59.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 44.0 | °C | ASTM D648 |
| Peak Melting Temperature | 127 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 6 B12^ F20 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Ultramid® B3L BK00464 | BASF Corporation | Nylon 6 | Ultramid® |
| Niche PA66M40BK | Niche Polymer, LLC | Nylon 66 | Niche |
| Hostacom HBG H01 NAT | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sumiliteresin® PR-50699 I | SBHPP | Phenolic | Sumiliteresin® |