Mablex 464
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Ravago Group |
| Trademark: | Mablex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tP6SQt_Mablex-464.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS blend medium heat resistant grade high gloss |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 60.0 | MPa | |
| Break | 48.0 | MPa | |
| Tensile Strain (Break) | 45 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 32 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ISO 306/A50 |
| -- | 124 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm, in Oil) | 24 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 48 | mm/min | FMVSS 302 |
| Flame Rating 1 | Internal Method | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | UL94 internally tested |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EPO-TEK® OG133-8 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Karina IVORY PVC COMPOUND 105770-35/1-CY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ RX05488 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| POLYFLON™ D-3A | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| SCHULABLEND® SCHULABLEND® (ABS/PA) M/MK 7102 GF20 | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |