Order Products : sales@su-jiao.com
Fiberfil® PP-60/FR
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tOqM2P_Fiberfil-PP-60-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®PP-60/FR is a polypropylene homopolymer (PP Homopoly) material,. This product is available in North America,. Fiberfil®The main features of PP-60/FR are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 - 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 1.0 - 1.2 | % | ASTM D955 |
| 6.35 mm | 1.2 - 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 - 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 2900 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 37.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 98.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.3 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 177 - 210 | °C | |
| Middle Temperature | 193 - 227 | °C | |
| Front Temperature | 188 - 221 | °C | |
| Nozzle Temperature | 188 - 221 | °C | |
| Processing (Melt) Temp | 193 - 216 | °C | |
| Mold Temperature | 32.2 - 54.4 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN ST900 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| TRIREX® 3026B(Q) | Samyang Corporation | PC | TRIREX® |
| Dialon 1520 | DTR S.r.l. (Develop Thermoplastic Resins) | PC | Dialon |
| Infino XP-2140C | SAMSUNG SDI CO., LTD. | PPS | Infino |
| Karina LILAC PVC COMPOUND 831-34/148-IS RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |