CP PRYME® Nylon 66 NN213HSL BK/OM200
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® Nylon 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tMGiva_CPPRYMENylon66NN213HSLBKOM200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 13% Glass Fiber Reinforced Utility Grade Nylon 6/6, Heat Stabilized, Lubricated, Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 117 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 260 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 243 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 271 - 293 | °C | |
| Middle Temperature | 271 - 293 | °C | |
| Front Temperature | 271 - 293 | °C | |
| Nozzle Temperature | 271 - 293 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 27 - 60 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME PP SPEXP64 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| ACCUTECH™ CP0436G20M10CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Hapflex™ 660-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Hostacom ETA5081 | LyondellBasell Industries | TPO (POE) | Hostacom |
| IPC PP 4800HMH | International Polymers Corporation | PP Homopolymer | IPC PP |