Braskem PE TU3001
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tKoCQy_Braskem-PE-TU3001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TU3001 is a low-density polyethylene (LDPE) with high molecular weight, excellent mechanical properties and good processability. These qualities ensure the production of films with uniform thickness. TU3001 resin is stabilized with a hindered amine (HALS) and antioxidants which warrants high resistance to aging caused for exposure to solar radiation. Films manufactured with TU3001 are colorless and have high light transmission. The films produced are transparent but not thermal. This product is identified as PE 115 according to ASTM D-4976-04a standard specification. Application: Films for greenhouses. Films for applications that require high mechanical strength and high resistance to aging from solar radiation (UV radiation exposure). Durability: Films manufactured with TU3001 has a minimum duration expectancy of 18 months (two winters and one summer) for continuing use in a greenhouse with a maximum solar radiation of 150 kLy (kcal/cm²/year) and at least 130?m. For another geographic region ask for help in our technical department. The suitable durability refers to the retention of at least 50% of the original mechanical resistance of a film produced with pure TU3001. The UV stabilizer used in TU3001 presents great chemical resistance for a range of pesticides, although compounds which have sulfur and halogens can reduce the films shelf life. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.14 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 150 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 50 µm, Blown Film | 150 | MPa | |
| 2% Secant, TD : 50 µm, Blown Film | 170 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 150 µm, Blown Film | 30.0 | MPa | |
| TD : Break, 150 µm, Blown Film | 25.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 150 µm, Blown Film | 360 | % | |
| TD : Break, 150 µm, Blown Film | 740 | % | |
| Dart Drop Impact (150 µm, Blown Film) | 410 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 150 µm, Blown Film | 470 | g | |
| TD : 150 µm, Blown Film | 700 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 150 µm, Blown Film) | 62 | ASTM D2457 | |
| Haze (150 µm, Blown Film) | 16 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Stabilizer | 5750 to 6500 | ppm | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 225 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 5 T 20 FRG 2 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Multilon® T-3615Q | TEIJIN LIMITED | PC+ABS | Multilon® |
| Delrin® 500T NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Europrene® 1778 | Versalis S.p.A. | SBR, Emulsion | Europrene® |
| Laticonther 57 CPG/550 | LATI S.p.A. | PPA | Laticonther |