Ultramid® B3EG6 FC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tK8YAR_Ultramid-B3EG6-FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3EG6 FC is a 30% glass fiber reinforced injection molding PA6 grade Applications Intended for food contact applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 50.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| Saturation | 6.6 | -- | % | ASTM D570 |
| Saturation, 23°C | 6.6 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.1 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9500 | 6200 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 172 | -- | MPa | ASTM D638 |
| Break, 23°C | 185 | 115 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 3.2 | -- | % | ASTM D638 |
| Break, 23°C | 3.5 | 8.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 8280 | -- | MPa | ASTM D790 |
| 23°C | 8600 | 5000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 270 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 15 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 95 | 110 | kJ/m² | |
| Notched Izod Impact | ||||
| -40°C | 96 | -- | J/m | ASTM D256 |
| 23°C | 110 | -- | J/m | ASTM D256 |
| 23°C | 15 | 20 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS FS | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Unichem 7811C-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| ALTECH® PA66 A 2030/516 GF30 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Lionpol LC-60063 | Lion Polymers Incorporated | TPE | Lionpol |
| POLYform C M20 | Polykemi AB | Acetal (POM) Copolymer | POLYform C |