LNP™ LUBRICOMP™ DCI06APW compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tIQtx8_LNP-LUBRICOMP-DCI06APW-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DCI06APW is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, High Flow. Also known as: LNP* LUBRICOMP* Compound DCI06APW Product reorder name: DCI06APW |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 28.0 | cm³/10min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.050 to 0.15 | % | |
| Across Flow : 24 hr | 0.15 to 0.40 | % | |
| Water Absorption (24 hr, 50% RH) | 0.11 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 25400 | MPa | ASTM D638 |
| -- | 23800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 183 | MPa | ASTM D638 |
| Break | 183 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.4 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 20100 | MPa | ASTM D790 |
| -- 5 | 20600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 262 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 265 | MPa | ASTM D790 |
| Compressive Strength | 128 | MPa | Internal Method |
| Shear Modulus | 3510 | MPa | ASTM C273 |
| Shear Strength | 92.0 | MPa | ASTM C273 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 94 | J/m | ASTM D256 |
| 23°C 7 | 9.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 500 | J/m | ASTM D4812 |
| 23°C 8 | 34 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 16.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 128 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 130 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.7E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.6E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 270 to 285 | °C | |
| Middle Temperature | 275 to 290 | °C | |
| Front Temperature | 285 to 300 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGH4000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Baoding 6126W | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| Durez® 33681 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| ESTABLEND 8500 | Cossa Polimeri S.r.l. | PC+ABS | ESTABLEND |
| SQUARE® SSR3918-60 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |