SABIC® LDPE HP2022J
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tHVniL_SABIC-LDPE-HP2022J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description HP2022 series resins are Low Density Polyethylene grades suitable for general purpose packaging. They exhibit better draw down, good opticals and mechanical properties. Typical Applications Thin shrink film, lamination film, produce bags, textile packaging, soft goods packaging, general purpose bags with good optics and t-shirts carrier bags. HP2022J: 750 ppm Slip & 1000 ppm Antiblock |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 30 µm, blown film | 160 | MPa | ASTM D882 |
| 1% secant, TD : 30 µm, blown film | 180 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 8.00 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 7.00 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 21.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 18.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 290 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 570 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 80 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 180 | g | ASTM D1922 |
| TD : 30 µm, blown film | 150 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 80 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured by producing 30 µ film with 2.5 BUR using 100% HP2022N. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8091 | Colorite Polymers | PVC, Unspecified | Unichem |
| Network Polymers PP PPB 25 0110 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| ADENE BHFBG | A.D. Compound spa | PP Copolymer | ADENE |
| Akulon® Ultraflow K-FG12 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| GERMAMID 6 HX | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |