MAJORIS DT267
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tHAvzG_MAJORIS-DT267.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DT267 is a 20% mineral filled polypropylene compound intended for injection moulding. The product is available in natural DT267 but other colours can be provided on request. DT267 has been developed especially for automotive interior parts that require excellent balance between the impact strength and stiffness and very good surface quality. In addition it has a good UV and weathering stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.5 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 112 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP BF335SA | Borealis AG | PP Copolymer | Borealis PP |
| ENGAGE™ 8540G | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| Latamid 66 MDT05-01 | LATI S.p.A. | Nylon 66 | Latamid |
| Paracril® BPLT | INSA | NBR | Paracril® |
| Kumho SAN SAN 300N A | Korea Kumho Petrochemical Co., Ltd. | SAN | Kumho SAN |