Tecnoprene® VK6 HIT1 NERO900
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Tecnoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tFbZvX_Tecnoprene-VK6-HIT1-NERO900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High fluidity polypropylene homopolymer reinforced with 31% chemically coupled glass fiber, high heat stabilization |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.20 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 6400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 148 | °C | ASTM D648 |
| Vicat Softening Temperature | 137 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANPRO® SM240 | Lotte Chemical Titan (M) Sdn. Bhd. | PP Impact Copolymer | TITANPRO® |
| 4MID® 9A24400 | 4Plas | Nylon 66 | 4MID® |
| Arnitel® PM650 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| Celstran® PA6-GF50-03 | Celanese Corporation | Nylon 6 | Celstran® |
| Durethan® BKV 15 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |