LNP™ THERMOCOMP™ LF008 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tFBAT2_LNP-THERMOCOMP-LF008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LF008 is a compound based on Polyetheretherketone resin containing 40% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound LF-1008 Product reorder name: LF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 3.0 | % | ASTM D955 |
| Across Flow : 24 hr | 1.1 | % | ISO 294-4 |
| Flow : 24 hr | 0.64 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13800 | MPa | ASTM D638 |
| -- | 12800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 2.07 | MPa | ASTM D638 |
| Yield | 156 | MPa | ISO 527-2 |
| Break | 154 | MPa | ASTM D638 |
| Break | 155 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.4 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2 |
| Break | 2.4 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 9650 | MPa | ASTM D790 |
| -- | 10400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 234 | MPa | ASTM D790 |
| -- | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 7.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 810 | J/m | ASTM D4812 |
| 23°C 3 | 54 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.6 | J | ASTM D3763 |
| -- | 3.68 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 261 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 861 TFE 8 | RTP Company | Acetal (POM) Copolymer | RTP |
| TECHNYL STAR™ AFX 218 V60 BLACK 31N | Solvay Engineering Plastics | Nylon 66 | TECHNYL STAR™ |
| Plenco 07202 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| PMC® 790 | Smooth-On, Inc | PUR, Unspecified | PMC® |
| PLASTRON™ PP-GF40-02 | Daicel Polymer Ltd. | PP, Unspecified | PLASTRON™ |