PLEXIGLAS® Sheet Clear 2890
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | PLEXIGLAS® Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tF1ESP_PLEXIGLAS-Sheet-Clear-2890.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UV transmitting PLEXIGLAS® GS is a kind of cast acrylic (= polymethylmethacrylate, PMMA) specially developed for tanning beds, with high UV (ultraviolet) transmission and UV resistance. UV transmitting PLEXIGLAS® GS has a perfectly coherent surface, whether in its smooth or satin-finished version. It always feels pleasantly warm to the skin and is hygienic. It is therefore ideally suited for use in both cosmetic and therapeutic UV appliances. The material is particularly resistant to extremes of climate, i. e. also ideal for applications exposed to heat and humidity in addition to UV radiation. UV transmitting PLEXIGLAS® GS exhibits high mechanical strength at low weight. Clear 2890 with specially adjusted UV transmission for special applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | > 2500 | MPa | ISO 527-2 |
| Tensile Stress (3.00 mm) | > 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 3.00 mm) | > 5.0 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/B |
| CLTE - Flow (0 to 50°C) | 7.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.19 | W/m/K | DIN 52612 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Fire Rating | |||
| -- | M4 | NF P 92501 | |
| -- | Class 3 | BS 476 Part 7 | |
| Normally flammable | B2 | DIN 4102 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | DIN 5036-3 | ||
| -- 1 | > 90.0 | % | |
| 3000 µm 2 | > 60.0 | % | |
| 8000 µm 3 | > 25.0 | % |
| Note Message | |
|---|---|
| 1 . | In the visible range |
| 2 . | In the UV range |
| 3 . | In the UV range |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stylac™ ID510 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| Axiall PVC HF-6597 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| KOPELEN JM-350 | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| LEXAN™ FXD9810 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ LUBRICOMP™ RFN18S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |