Zythane® 7090A
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Alliance Polymers & Services |
| Trademark: | Zythane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tEiRyl_Zythane-7090A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zythane 7090A is a polyether--based TPU specifically formulated for extrusion applications with ease of processing. It exhibits excellent abrasion resistance and toughness and has good hydrolytic stability, oil, fuel and solvent resistance. It is supplied uncolored in pellet form. Typical Applications: Zythane 7090A applications include among others FDA applications, cable sheathing, spiral and pneumatic tubing, film, irrigation hoses, conveyor hoses, fire hoses, hydraulic hoses, cable jacketing, flat flex cables, automotive sensor cables. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 90 | ASTM D2240 | |
| Shaw D | 40 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance | 40.0 | mg | ASTM D1044 |
| Abrasion - DIN | 20 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 8.00 | MPa | ASTM D412 |
| 300% strain | 15.0 | MPa | ASTM D412 |
| Tensile Strength (Break) | 39.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 460 | % | ASTM D412 |
| Tear Strength 1 | 132 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 24°C, 22 hr | 23 | % | ASTM D395B |
| 70°C, 72 hr | 41 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -37.2 | °C | DSC |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 185 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 205 | °C | |
| Nozzle Temperature | 205 - 215 | °C | |
| Processing (Melt) Temp | 205 - 215 | °C | |
| Mold Temperature | 25.0 - 60.0 | °C | |
| Back Pressure | 0.500 - 1.00 | MPa | |
| Screw Speed | 60 - 200 | rpm | |
| Clamp Tonnage | 4.1 - 6.9 | kN/cm² |
| Injection instructions |
|---|
| Injection Speed: >.4 in/sec |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 185 | °C | |
| Cylinder Zone 2 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 205 | °C | |
| Die Temperature | 212 | °C |
| Extrusion instructions |
|---|
| Gate Temperature: 205°C (401°F) |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BX30WT6617 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Novalloy-A A1300 | PlastxWorld Inc. | ABS+Nylon | Novalloy-A |
| Celstran® +PP-GF60-04CN15/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| G-PAEK™ 1460GF | Gharda Chemicals Ltd. | PEK | G-PAEK™ |
| Hipolyene 1046 NM | Zylog Plastalloys | TPO (POE) | Hipolyene |