NORYL™ GFN2F resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tETuoD_NORYL-GFN2F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPE+PS blend. 20% Glass reinforced. UL746C F1. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings and impellers, valve components and others. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 8.10 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.50 | % | Internal Method |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6200 | MPa | ASTM D638 |
| -- | 7070 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 90.0 | MPa | ASTM D638 |
| Break | 97.3 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.6 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 5800 | MPa | ASTM D790 |
| -- 5 | 6540 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 167 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -40°C | 96 | J/m | ASTM D256 |
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 7 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 650 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 22.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 143 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 8 | 143 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 9 | 137 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ISO 306/B50 |
| -- | 146 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.3E-5 | cm/cm/°C | |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.86 | ||
| 60 Hz | 2.86 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 8.0E-4 | ||
| 60 Hz | 8.0E-4 | ||
| Arc Resistance 10 | PLC 7 | ASTM D495 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 | |
| Oxygen Index | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 266 to 316 | °C | |
| Middle Temperature | 277 to 321 | °C | |
| Front Temperature | 288 to 327 | °C | |
| Nozzle Temperature | 299 to 327 | °C | |
| Processing (Melt) Temp | 299 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 120*10*4 mm |
| 9 . | 120*10*4 mm |
| 10 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-9710U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Badamid® LB70 K | Bada AG | Nylon 6 | Badamid® |
| ALTECH® PA6 A 1000/110 IM | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Polimid A 30 GF V0A | Poliblend S.p.a. | Nylon 66 | Polimid A |
| 3M™ Dyneon™ Fluoroelastomer FC 1610N | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |