LNP™ STAT-KON™ DD0009XP compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tEPoN1_LNPSTATKONDD0009XPcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON D-FR is a compound based on Polycarbonate resin containing Carbon. Added features of this grade include: Flame Retardant, Electrically Conductive. Also known as: LNP* STAT-KON* Compound D-FR Product reorder name: DD0009XP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.21 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2510 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 69.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/5 |
| Fracture 2 | 46.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 4.7 | % | ASTM D638 |
| Yield | 4.7 | % | ISO 527-2/5 |
| Fracture 4 | 13 | % | ASTM D638 |
| Fracture | 11 | % | ISO 527-2/5 |
| Flexural Modulus 5 | 2520 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 6 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1700 | J/m | ASTM D4812 |
| 23°C 7 | 150 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 33.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 139 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 8 | 138 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 130 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 9 | 126 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0 - 8.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 254 - 266 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 254 - 288 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADEKA YG-108 | Adeka Corporation | PUR-Ester | ADEKA |
| APEX® 79-B085-C | Teknor Apex Company | PVC, Flexible | APEX® |
| LNP™ STAT-KON™ FX98500C compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ STAT-KON™ |
| Plasmer 5065N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| ExxonMobil™ LLDPE LL 1001 Series | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |