LNP LUBRICOMP KL002 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound KL-4020 Product reorder name: KL002 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2550 | MPa | ASTM D638 |
| Tensile Strength (Break) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 9.7 | % | ASTM D638 |
| Flexural Modulus | 2370 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 560 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 92.2 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 HV 11 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Telcar® TL-2440F | Teknor Apex Company | TPE | Telcar® |
| Spartech Polycom SCR7-7022F | Spartech Polycom | PC | Spartech |
| Huafon JF-P-501 / JF-I-601 | Huafon Group Co., Ltd. | PUR-Ether | Huafon |
| Petrotene® PP A3 T20 BRC0003 PH377 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |