LNP™ THERMOCOMP™ DX06313 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tDAnIw_LNP-THERMOCOMP-DX06313-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate base, 30% glass fiber reinforced, impact modified material. Thinwall housing, mobile phone. Some light color grades may have lower impact data than nature and black grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 300°C/1.2 kg | 4.6 | g/10 min | |
| 300°C/5.0 kg | 42 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 32.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.50 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7500 | MPa | ASTM D638 |
| -- | 7420 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 99.0 | MPa | ASTM D638 |
| Break | 90.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 3.6 | % | ASTM D638 |
| Break | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 7000 | MPa | ASTM D790 |
| -- 5 | 6650 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 170 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 120 | J/m | ASTM D256 |
| 23°C, Light & White Colors | 90 | J/m | ASTM D256 |
| 23°C, Natural & Black Colors | 190 | J/m | ASTM D256 |
| -30°C 8 | 12 | kJ/m² | ISO 180/1A |
| 23°C 9 | 17 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 24.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 136 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 136 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ASTM D1525, ISO 306/B50 11 11 |
| -- | 143 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Nozzle Temperature | 310 to 332 | °C | |
| Processing (Melt) Temp | 316 to 338 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP M1701 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| T-Blend® 5503N-PE | TSRC Corporation | TPE | T-Blend® |
| DOMAMID® 66G30HR | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| DOWLEX™ 2342M | The Dow Chemical Company | HDPE | DOWLEX™ |
| LNP™ LUBRICOMP™ LX92134 compound | SABIC Innovative Plastics Europe | PEEK | LNP™ LUBRICOMP™ |