Order Products : sales@su-jiao.com
Ravamid® A MF25 BK45
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ravago Group |
| Trademark: | Ravamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tBghB9_Ravamid-A-MF25-BK45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Black, 25% mineral filled, general purpose All the products are also available Heat Stabilized (H) and UV Stabilized (UV) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.55 to 0.85 | % | ASTM D955 |
| Humidity | < 0.20 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 55.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.2 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 75 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (Area) (23°C) | 7.00 | kJ/m² | ASTM D256 |
| Notched Izod Impact Strength (23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 235 | °C | ISO 306/B50, ASTM D1525 1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (3.20 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® 103HSL BKB080 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Avantra® 8731 | PMC Group Polymer Products | PS (HIPS) | Avantra® |
| Badaprop® PPH50 FR EL Schwarz | Bada AG | PP Homopolymer | Badaprop® |
| LEXAN™ HF1140R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| DAI-EL™ G-952 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |