HiFill® PA4/6 CF40 IM HS
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tAfH9n_HiFill-PA4-6-CF40-IM-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PA4/6 CF40 IM HS is a Polyamide 46 (Nylon 46) product filled with 40% carbon fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.33 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Break) | 241 | 207 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.7 | 3.2 | % | ASTM D638 |
| Flexural Modulus | 22100 | 18600 | MPa | ASTM D790 |
| Flexural Strength | 393 | 345 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | 100 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 282 | -- | °C | ASTM D648 |
| CLTE - Flow | 1.8E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 10 | -- | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 282 to 316 | °C | |
| Middle Temperature | 282 to 316 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Processing (Melt) Temp | 246 to 316 | °C | |
| Mold Temperature | 87.8 to 127 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2405 MAS048 | Covestro - Polycarbonates | PC | Makrolon® |
| NEFTEKHIM PE 6750H (506H8) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Next Nylon 66 Prime Series PMG38-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Braskem PP RP 340S | Braskem | PP Random Copolymer | Braskem PP |
| OTECH TPR OTR7000-Sandal | OTECH Corporation | TPE | OTECH TPR |