AT 280
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | AT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tANOtw_AT-280.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AT 280 is a low density polyethylene material,. This product is available in North America, and the processing method is: composite. The main characteristics of AT 280 are: contact with food. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 94 | ASTM D2240 | |
| Shaw D | 47 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 7.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 220 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 190 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -25.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 87.0 | °C | ASTM D1525 |
| Melting Temperature | 105 | °C | DSC |
| Additional Information |
|---|
| The value listed as Density-Specific Gravity, ASTM D1505, was also tested in accordance with ASTM D1928 Proc A.Ring & Ball Softening Point, ASTM E28: 130°C |
| Note Message | |
|---|---|
| 1 . | Type 4, 50mm/min |
| 2 . | Type 4, 50mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® BS 200 Black | Radici Plastics | Nylon 6 | Radilon® |
| Network Polymers PP NPP 20-1202M | Network Polymers, Inc. | PP Random Copolymer | Network Polymers PP |
| ADDILENE H 555 Y7 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Karina YELLOW PVC COMPOUND 602D02/101-C-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ULTEM™ 1285 resin | SABIC Innovative Plastics | PEI | ULTEM™ |