PermaStat® 201
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | PermaStat® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t9GAfI_PermaStat-201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1790 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.5 | % | ASTM D638 |
| Flexural Modulus | 1790 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 51.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1300 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+9 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, ASTM D 955, 3.175mm: 5-8mm/mTensile Elongation, ASTM D 638: 4-7%Static Decay, FTMS-4046.1, Mil B-81705C: <2.0 seconds |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 274 - 288 | °C | |
| Middle Temperature | 274 - 288 | °C | |
| Front Temperature | 274 - 288 | °C | |
| Mold Temperature | 66.0 - 107 | °C | |
| Injection Pressure | 82.9 - 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1745N | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sipolprene® 72220 W | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Vydyne® R530H NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| POLYfill PPC T2020 | Polykemi AB | PP Copolymer | POLYfill |
| Osterlene® PPH20NA | Osterman & Company | PP Homopolymer | Osterlene® |