DOWLEX™ 2036.01G
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t8vXx0_DOWLEX-2036-01G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2036.01G Linear Low Density Polyethylene Resin is suitable for the production of cast films with high stiffness, good tear strength and outstanding toughness. It can be used in skin layers of coextreuded cast films made from DOWLEX resins to provide a surface with good slip properties. Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.933 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance | 10.3 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 324 | J/cm³ | ASTM D882 |
| TD | 308 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 16.9 | MPa | ASTM D882 |
| TD : Yield | 17.6 | MPa | ASTM D882 |
| MD : Fracture | 59.2 | MPa | ASTM D882 |
| TD : Fracture | 39.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 620 | % | ASTM D882 |
| TD : Fracture | 750 | % | ASTM D882 |
| Dart Drop Impact | 57 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 83 | g | ASTM D1922 |
| TD | 290 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 119 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 90 | ASTM D2457 | |
| Haze | 2.6 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 274 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film: EGAN/Davis-Standard 5 layer cast line Melt Temperature: 525°F (274°C) Chill Roll (primary/secondary) Temperature: 70°F (21°C) Line Speed: 600 fpm (183m/min) Die Width: 24in. (520mm) Die Gap: 25mil (0.6mm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 A | RTP Company | Nylon 6 | RTP |
| Ravago Compounds HMP-366 | Ravago Manufacturing Americas, LLC | EVA | Ravago Compounds |
| TEREZ PA 6.6 7500 GF 25 H | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| FORMULA P ELAN 6220 M2 Z | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Karina COMP. PVC CRYSTAL -E 80/204-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |