| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem IDESA |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t8lwvL_BraskemPELDF2023.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDF2023 is a non-additivated low density polyethylene. It has good optical properties and excellent processability. Applications: Bags and sacks, Shrink Film, Blown Film, Cast Film and Food Packaging Films. Process: Blown Film, Cast Film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 145 | MPa | ASTM D882 |
| 1% secant, TD | 145 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 30.0 | MPa | ASTM D882 |
| TD : Fracture | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 490 | % | ASTM D882 |
| TD : Fracture | 1100 | % | ASTM D882 |
| Dart Drop Impact | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 480 | g | ASTM D1922 |
| TD | 150 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 100 | ASTM D2457 | |
| Haze (50.0 µm) | < 6.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CGPC PVC H-61 | China General Plastics Corporation | PVC, Unspecified | CGPC PVC |
| Cri-Line GP-715-BL | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| LEXAN™ 172L resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| PLUSTEK PA112NT | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Plenco 01530 (Transfer) | Plastics Engineering Co. | Polyester, TS | Plenco |