Stratasys ABS-M30i
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Stratasys |
| Trademark: | Stratasys |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t8Sc83_Stratasys-ABS-M30i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Production-Grade Thermoplastic for Fortus 3D Production Systems ABS-M30i is a high strength material well suited for the medical, pharmaceutical and food packaging industries. Parts manufactured with ABS-M30i material are biocompatible (ISO 10993 USP Class VI) and can be gamma or EtO sterilized. When combined with Fortus® 3D Production Systems, ABS-M30i gives you biocompatible Real Parts™ with excellent mechanical properties that are well suited for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Thickness - Layer Capability | 127.0 to 330.2 | µm |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistance 1 | 6.0E+13 to 1.5E+14 | ohms | ASTM D257 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(3.18 mm) | 2410 | MPa | ASTM D638 |
| Tensile Strength 3(3.18 mm) | 35.9 | MPa | ASTM D638 |
| Tensile Elongation 4(Break, 3.18 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 5 | 2320 | MPa | ASTM D790 |
| Flexural Strength 6 | 60.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 140 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C) | 280 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 95.6 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 82.2 | °C | |
| Glass Transition Temperature | 108 | °C | DSC |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 7 |
| CLTE | ASTM E831 | ||
| Flow | 8.8E-5 | cm/cm/°C | |
| Transverse | 8.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 3.1 to 15 | kV/mm | ASTM D149 |
| Dielectric Constant 8 | 2.70 to 2.90 | ASTM D150 | |
| Dissipation Factor 9 | 5.1E-3 to 5.3E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | Type I, 5.1 mm/min |
| 5 . | Method I (3 point load), 1.3 mm/min |
| 6 . | Method I (3 point load), 1.3 mm/min |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| 8 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 9 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V972 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Ultraform® N 2320 0035 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| APEX® 88-N131M-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Axiall PVC NR-5009 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| SQUARE® LSR6915-80A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |