ULTEM™ 4001 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t8M6kk_ULTEM4001resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 9.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| K (wear) Factor | Internal method | ||
| -- 1 | 27.0 | Internal method | |
| -- 2 | 72.0 | Internal method | |
| PV Limit 3 | 1.9 | MPa·m/s | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 4 | 3360 | MPa | ASTM D638 |
| Tensile Strength 5(Yield) | 103 | MPa | ASTM D638 |
| Tensile Elongation 6(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 7(100 mm Span) | 3410 | MPa | ASTM D790 |
| Flexural Strength 8(Yield, 100 mm Span) | 152 | MPa | ASTM D790 |
| Coefficient of Friction (vs. Steel - Dynamic) | 0.25 | ASTM D1894 | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 2.00 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 1300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 200 | °C | ASTM D648 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI | 170 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 9 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.381 mm | V-0 | UL 94 | |
| 1.50 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 338 - 360 | °C | |
| Middle Temperature | 343 - 366 | °C | |
| Front Temperature | 349 - 371 | °C | |
| Nozzle Temperature | 349 - 371 | °C | |
| Processing (Melt) Temp | 349 - 371 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | xE-10, PV=2000 psi-fpm vs Self |
| 2 . | xE-10, PV=2000 psi-fpm vs Steel |
| 3 . | 0.51 m/s |
| 4 . | 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 2.6 mm/min |
| 9 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T40P200-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sylvin 8867-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Veradel® 3250 | Solvay Specialty Polymers | PESU | Veradel® |
| Galloo GP-PP-157 | Galloo Plastics | PP, Unspecified | Galloo |
| Gallonprene® GP200-8 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |