| 30% glass fiber reinforced ABS compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 7.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 147 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 81.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6900 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 1.9% strain | 106 | MPa | ISO 178 |
| 2.0% strain 3 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 14 | kJ/m² | ISO 179/1eU |
| 23°C | 12 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 99.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 95.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ISO 306/A50 |
| -- | 102 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.6 mm | HB | IEC 60695-11-10, -20 | |
| 3.2 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.5 mm | 700 | °C | IEC 60695-2-13 |
| 3.0 mm | 700 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 40 - 80 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | at Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APTIV® 1300 | Victrex plc | PEEK | APTIV® |
| Axiall PVC 9113 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Axiall PVC 8266 White | Axiall Corporation | PVC, Rigid | Axiall PVC |
| CYROLITE® G-20 | Evonik Cyro LLC | Acrylic (PMMA) | CYROLITE® |
| Geon™ Vinyl Wire & Cable WJCK435 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |