Ultrason® S 3010
| Category: | PSU , Polysulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t88nfN_Ultrason-S-3010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultrason S 3010 is medium viscosity injection molding grade with improved toughness and chemical resistance (stress crack resistance). Applications Typical applications include laboratory accessories and household parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.74 | % | |
| Flow | 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 135 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2550 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 6.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 5.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 5.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 177 | °C | ISO 75-2/A |
| CLTE - Flow | 5.3E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 1.60 mm | 155 | °C | |
| 3.00 mm | 155 | °C | |
| RTI Imp | UL 746 | ||
| 1.60 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Str | UL 746 | ||
| 1.60 mm | 155 | °C | |
| 3.00 mm | 155 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 37 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.10 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 8.0E-4 | ||
| 1 MHz | 6.4E-3 | ||
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 340 to 390 | °C | |
| Mold Temperature | 140 to 180 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® VEP30C | BASF Leuna GmbH | Nylon 6 | Miramid® |
| VITAMIDE® AK20BK6424 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| BP RPP 3015 T NAT | Buckeye Polymers, Inc. | PP, Unspecified | BP |
| Braskem PP H 118 | Braskem | PP Homopolymer | Braskem PP |
| Enviramid® N2330HLUV2 BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |