DENKA Transparent Polymer TE-10S
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA Transparent Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t7gKcB_DENKA-Transparent-Polymer-TE-10S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DENKA Transparent Polymer TE-10S is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 200°C/5.0 kg | 1.7 | g/10 min | |
| 220°C/10.0 kg | 25 | g/10 min | |
| Molding Shrinkage (2.00 mm) | 0.50 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 46 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 42.0 | MPa | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 31 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2000 | MPa | ISO 178 |
| Flexural Stress 2 | 63.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 87.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 91.0 | % | ISO 13468-1 |
| Haze (2000 µm) | 1.5 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3548 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| ALAMID® 6.6 MF 40 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| Amodel® A-1625 HS | Solvay Specialty Polymers | PPA | Amodel® |
| Fainplast PVC RL 708 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Huafon HF-1075AP | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |