Michithene R6100
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michithene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t76T1s_Michithene-R6100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michithene R6100 is a Low Density Polyethylene product. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 8.96 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Flexural Modulus - Tangent | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 204 | °C | |
| Middle Temperature | 204 | °C | |
| Front Temperature | 199 | °C | |
| Nozzle Temperature | 210 | °C | |
| Processing (Melt) Temp | 204 | °C | |
| Mold Temperature | 26.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA6G40HSL-BK10 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| NOVA PC 9050V | NOVA Polymers, Inc. | PC | NOVA PC |
| LNP™ THERMOCOMP™ MFB41I compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ THERMOCOMP™ |
| THERMOLAST® V TV8VAN (Series: LTP/PA) | KRAIBURG TPE | TPE | THERMOLAST® V |
| Moplen EP332K | PolyMirae | PP Impact Copolymer | Moplen |