Orevac® T 9305
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Orevac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t68yrm_Orevac-T-9305.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OREVAC® T 9305 is a random terpolymer of ethylene, vinyl acetate and maleic anhydride made by high-pressure radicalar polymerization process. As an ethylene copolymer, OREVAC® T 9305 is compatible with PE in all proportions, and with most other ethylene copolymers. Vinyl acetate brings softness, flexibility and polarity, maleic anhydride gives reactivity, leading to versatile adhesive properties to polar and non polar substrates. Applications OREVAC® T 9305 is compatible with most tackifying resins and waxes and can be used for hot melt adhesives formulations. OREVAC® T 9305 is also suitable to produce thermo-adhesive films for solid substrates like PA, PET & PU films, aluminium foils... |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 150 to 210 | g/10 min | ASTM D1238, ISO 1133 |
| Vinyl Acetate Content | 26.0 to 30.0 | wt% | |
| Maleic Anhydride Content | 6400 | ppm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ring and Ball Softening Point | 92 | °C | ASTM E28 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec, 2.80 mm, Compression Molded) | 75 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break, 2.80 mm, Compression Molded 1 | 5.50 | MPa | ASTM D638 |
| Break, 2.80 mm, Compression Molded | 5.50 | MPa | ISO 527-2/5A/50 |
| Tensile Elongation | |||
| Break, 2.80 mm, Compression Molded 2 | 700 to 900 | % | ASTM D638 |
| Break, 2.80 mm, Compression Molded | 700 to 900 | % | ISO 527-2/5A/50 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | < 40.0 | °C | ISO 306/A, ASTM D1525 3 |
| Melting Temperature | 68.0 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMACOR™ 3002 | The Dow Chemical Company | EAA | PRIMACOR™ |
| Small Boss HS-105-2 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Flexible | Small Boss |
| Petrothene® M2512 | LyondellBasell Industries | LDPE | Petrothene® |
| ESTOPLAST SR 4000NN01 | Ester Industries Ltd. | ABS | ESTOPLAST SR |
| VALOX™ 457 resin | SABIC Innovative Plastics | PBT | VALOX™ |