LNP™ THERMOCOMP™ OF008 compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t3gEy2_LNPTHERMOCOMPOF008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP OF008 is a compound based on PPS - Linear resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound OF1008L Product reorder name: OF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 0.80 - 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.20 - 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 159 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 12900 | MPa | ISO 178 |
| Flexural Stress | 233 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 278 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 252 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PFA D 335D | DuPont Fluoropolymers | PFA | Teflon® PFA |
| CALFIN 1152CF | Pooya Polymer Tehran | Polyolefin, Unspecified | CALFIN |
| DINALON® A1S25 G35 (Glass) | Grupo Repol | Nylon 66 | DINALON® |
| ELASTOSIL® RT 480 | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| LARIPUR® LPR 5225 | COIM S.p.A. | TPU-Polyester | LARIPUR® |