Order Products : sales@su-jiao.com

Sasol Polymers PP CMR348

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	Sasol Polymers
Trademark:	Sasol Polymers PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	t25yXN_Sasol-Polymers-PP-CMR348.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features

Medium flow

Specifically recommended for the manufacture of cylindrical containers up to 5 litres in capacity

Excellent top loading performance as well as good toughness

Contains a nucleating agent which ensures rapid crystallisation, resulting in an improved impact to stiffness balance as well as shorter cooling times

Applications
Injection moulding

Paint containers

Household and domestic articles

Outdoor stadium seating

Furniture components

General Information
Additive	Nucleating agent Antistatic property Unspecified additive
Features	Nucleated Impact copolymer Antistatic property Medium liquidity Good toughness Compliance of Food Exposure
Uses	Outdoor furniture Furniture Household goods Container
Agency Ratings	EC 1935/2004 FDA 21 CFR 177.1520(a)(3)(i)(c)(1) FDA 21 CFR 177.1520(c) 3.1a
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	8.5	g/10 min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction	1.3	%	ISO 294-4
Flow direction	1.4	%	ISO 294-4

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	62.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1450	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	28.0	MPa	ISO 527-2/1A/50
Tensile Strain			ISO 527-2/1A/50
Yield	6.0	%	ISO 527-2/1A/50
Fracture	> 50	%	ISO 527-2/1A/50
Flexural Modulus	1400	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-20°C	3.5	kJ/m²	ISO 179/1eA
0°C	5.0	kJ/m²	ISO 179/1eA
23°C	10	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	90.0	°C	ISO 75-2/B
1.8 MPa, not annealed	52.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	152	°C	ISO 306/A120
--	68.0	°C	ISO 306/B120
Melting Temperature	163	°C	ISO 11357-3

Injection	Nominal Value	Unit
Hopper Temperature	40.0 - 60.0	°C
Rear Temperature	180 - 260	°C
Middle Temperature	220 - 280	°C
Front Temperature	240 - 280	°C
Nozzle Temperature	220 - 280	°C
Processing (Melt) Temp	220 - 280	°C
Mold Temperature	20.0 - 60.0	°C

Injection instructions
Zone 4: 240 to 280°C

Resin Grade	Manufacturer	Category	Trademark
Maxxam™ PP FR 7380-8001-ISO	PolyOne Corporation	PP, Unspecified	Maxxam™
PTS POM-90	Polymer Technology and Services, LLC	Acetal (POM) Copolymer	PTS
Sevrene® 6750-70A	Vi-Chem Corporation	TPE	Sevrene®
DJSilicone NE-3270	DONGJUE SILICONE (NANJING) CO., LTD	Silicone	DJSilicone
Sylvin 8250-75UV White 1575	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin