E-RIALGLASS H 15 S 30 TG
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALGLASS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t1AYBL_E-RIALGLASS-H-15-S-30-TG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer obtained by partial selected industrial scraps recycling; 30% talc and glass fiber reinforced, chemically coupled. High flowability, specific for injection molding of complex particulars; excellent thermal and mechanical properties. Available in black and natural version and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 0.50 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.020 | % | ISO 62 |
| Ash Content | 30 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 6.3 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 60.0 | MPa | ISO 527-2/20 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2/20 |
| Flexural Modulus 2(23°C) | 4700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 27 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 4.6 | kJ/m² | |
| 23°C | 6.3 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 21 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren N220 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Hostacom EKC 265N G71350 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LINATHENE® LL120C | USI Corporation | LLDPE | LINATHENE® |
| Sylvin 5150-90 Green 3129 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOPAS® 9506F-500 | Polyplastics Co., Ltd. | COC | TOPAS® |